| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 86.6 | 70.0 | 1037 | 78.5 | 55.0 | 599 | ||
| 86.3 | 69.5 | 1017 | 78.2 | 54.5 | 589 | ||
| 86.1 | 69.0 | 997 | 77.9 | 54.0 | 579 | ||
| 85.8 | 68.5 | 978 | 77.7 | 53.5 | 570 | ||
| 85.5 | 68.0 | 959 | 77.4 | 53.0 | 561 | ||
| 85.2 | 67.5 | 941 | 77.1 | 52.5 | 551 | ||
| 85.0 | 67.0 | 923 | 76.9 | 52.0 | 543 | ||
| 84.7 | 66.5 | 906 | 76.6 | 51.5 | 534 | ||
| 84.4 | 66.0 | 889 | 501 | 76.3 | 51.0 | 525 | |
| 84.1 | 65.5 | 872 | 494 | 76.1 | 50.5 | 517 | |
| 83.9 | 65.0 | 856 | 488 | 75.8 | 50.0 | 509 | |
| 83.6 | 64.5 | 840 | 481 | 75.5 | 49.5 | 501 | |
| 83.3 | 64.0 | 825 | 474 | 75.3 | 49.0 | 493 | |
| 83.1 | 63.5 | 810 | 468 | 75.0 | 48.5 | 485 | |
| 82.8 | 63.0 | 795 | 461 | 74.7 | 48.0 | 478 | |
| 82.5 | 62.5 | 780 | 455 | 74.5 | 47.5 | 470 | |
| 82.2 | 62.0 | 766 | 449 | 74.2 | 47.0 | 463 | |
| 82.0 | 61.5 | 752 | 442 | 73.9 | 46.5 | 456 | |
| 81.7 | 61.0 | 739 | 436 | 73.7 | 46.0 | 449 | |
| 81.4 | 60.5 | 726 | 430 | 73.4 | 45.5 | 443 | |
| 81.2 | 60.0 | 713 | 424 | 73.2 | 45.0 | 436 | |
| 80.9 | 59.5 | 700 | 418 | 72.9 | 44.5 | 429 | |
| 80.6 | 59.0 | 688 | 413 | 72.6 | 44.0 | 423 | |
| 80.3 | 58.5 | 676 | 407 | 72.4 | 43.5 | 417 | |
| 80.1 | 58.0 | 664 | 401 | 72.1 | 43.0 | 411 | |
| 79.8 | 57.5 | 653 | 396 | 71.8 | 42.5 | 405 | |
| 79.5 | 57.0 | 642 | 391 | 71.6 | 42.0 | 399 | |
| 79.3 | 56.5 | 631 | 385 | 71.3 | 41.5 | 393 | |
| 79.0 | 56.0 | 620 | 380 | 71.1 | 41.0 | 388 | |
| 78.7 | 55.5 | 609 | 375 | 70.8 | 40.5 | 382 | |
Tebulo losinthira mtengo wa kuuma kwa zinthu zachitsulo
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 370 | 70.5 | 40.0 | 377 | 269 | 28.0 | 274 | |
| 365 | 70.3 | 39.5 | 372 | 266 | 27.5 | 271 | |
| 360 | 70.0 | 39.0 | 367 | 263 | 27.0 | 268 | |
| 355 | 38.5 | 362 | 260 | 26.5 | 264 | ||
| 350 | 38.0 | 351 | 257 | 26.0 | 261 | ||
| 345 | 37.5 | 352 | 254 | 25.5 | 258 | ||
| 341 | 37.0 | 347 | 251 | 25.0 | 255 | ||
| 336 | 36.5 | 342 | 248 | 24.5 | 252 | ||
| 332 | 36.0 | 338 | 245 | 24.0 | 249 | ||
| 327 | 35.5 | 333 | 242 | 23.5 | 246 | ||
| 323 | 35.0 | 329 | 240 | 23.0 | 243 | ||
| 318 | 34.5 | 324 | 237 | 22.5 | 240 | ||
| 314 | 34.0 | 320 | 234 | 22.0 | 237 | ||
| 310 | 33.5 | 316 | 232 | 21.5 | 234 | ||
| 306 | 33.0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32.5 | 308 | 227 | 20.5 | 229 | ||
| 298 | 32.0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31.5 | 300 | 222 | 19.5 | 223 | ||
| 291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
| 287 | 30.5 | 292 | 218 | 18.5 | 218 | ||
| 283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
| 280 | 29.5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
| 273 | 28.5 | 278 | |||||
Zindikirani:
1. Kulimba kwa Brinell: Kumagwiritsidwa ntchito makamaka poyesa kulimba kwa zinthu zotayidwa, zoyikira, zitsulo zopanda chitsulo, ma billet otenthedwa ndi zinthu zonyowa. Mulingo woyezera ndi ≥HB450.
2. Kulimba kwa Rockwell: HRA imagwiritsidwa ntchito makamaka pa zitsanzo zolimba kwambiri kuti ziyeze kulimba kwa pamwamba pa zinthu ndi malo okhala ndi kulimba kwakukulu kuposa HRC67, monga carbide yopangidwa ndi simenti, chitsulo chopangidwa ndi nitride, ndi zina zotero. Mulingo woyezera ndi HRA>70. HRC imagwiritsidwa ntchito makamaka poyeza kulimba kwa zigawo zachitsulo (monga chitsulo cha carbon, chitsulo cha zida, chitsulo cha alloy, ndi zina zotero) pambuyo pozimitsa kapena kutenthetsa. Mulingo woyezera ndi HRC20~67.
3. Kulimba kwa Vickers: kumagwiritsidwa ntchito poyesa kulimba kwa zigawo zoonda ndi zigawo za mbale zachitsulo, ndipo kungagwiritsidwenso ntchito poyesa kulimba kwa zigawo zouma pamwamba monga carburizing, cyaniding, ndi nitriding.